Isomerization of c10-c14 hydrocarbons with fluorided metal-alumina catalyst

ABSTRACT

A method for preparing a hydrocarbon conversion catalyst by providing a composite composed of alumina having associated therewith a Group VIB, VIIB or VIII metal or compound and contacting the composite with an activator system comprising hydrogen and sulfuryl fluoride or thionyl fluoride. The catalysts so prepared are useful in such hydrocarbon conversion processes as isomerization, hydrocracking, reforming, alkylation, disproportionation, polymerization and hydrogenation.

United States Patent l Kravitz et al.

[ Oct. 22, 1974 I ISOMERIZATION or C -C HYDROCARBONS WITH FLUORIDED METAL-ALUMINA CATALYST [75] Inventors: Stanley Kravitz, Wiccopee; John H.

Estes; Robert M. Suggitt, both of Wappingers Falls, all of NY.

[73] Assignee: Texaco Inc., New York, NY.

[22] Filed: Jan. 26, 1972 [2!] Appl. No: 221,025

Related US. Application Data [62] Division of Ser. No. 48,899, June 25, 1970 Pat. No.

[52] U.S. Cl. 260/683.68, 208/112, 260/672 T [5 1] Int. Cl. i. C07c 5/30 [58] Field of Search 260/683.68; 208/120, 122, 208/123, 124; 252/442 [56] References Cited UNITED STATES PATENTS 3.092676 6/l963 Hettingcr Jr. et al 260/683.68

3,125,508 3/]964 Adlington et all 208/115 3.215.753 ll/l965 Bloch et al Zoo/683.68 3.338 843 8/1967 Gohle ct al. Mil/683.68

Primary ExaminerDelbert E. Gantz Assistant Examiner-G. J. Crasanakis Attorney, Agent, or FirmT. H. Wlhaley; C. G. Ries 5 7 ABSTRACT A method for preparing a hydrocarbon conversion catalyst by providing a composite composed of alumina having associated therewith a Group VlB, VllB 10 Claims, No Drawings 1 ISOMERIZATION OF C, C, HYDRUCXRIIUNS WITH F LUORIDED METAL-ALUMINA CATALYST This application is a division of application Ser. No. 48,899, filed June 25, I970, now US. Pat. No. 3,692,697.

BACKGROUND OF'THE INVENTION This invention relates to the preparation of fluorine containing catalysts and to their use in low temperature hydrocarbon conversion processes. In one of its specific aspects, this invention relates to a method of preparing a catalyst comprising a member of Group VIB, VIIB or VIII of the Periodic Table, alumina and fluorine which is suitable for the conversion of hydrocarbons.

Fluorided catalysts are of interest for various processes including isomerization, reforming, alkylation, hydrogenation, disproportionation, cracking, polymerization and hydrocracking. Heretofore, activation of catalyst bases or composites by fluoriding was undertaken employing aqueous hydrogen fluoride or vaporized boron or ammonium fluorides. such fluoriding techniques, however, by virtue of the fluoriding materials employed introduced various problems not the least of which included health, handling and equipment corrosion. In some instances unwanted surface deposits resulted from the treatment which interferred with the catalysts ability to function. Moreover, such fluoriding techniques did not lend themselves to the replacement of fluorine lost during high temperature regeneration. Recently, other fluoriding compounds have been suggested such as carbon tetrafluoride and sulfur tetrafluo- I ride. However, these materials in addition to their costliness present physiological difficulties.

It is therefore an object of this invention to provide a method for catalytically activating a composite material employing as a component of the activator system fluoriding agents that introduce no equipment corrosion problems.

Another object of this invention is to provide a method for fluoriding catalysts with agents that are physiologically inert.

Yet another object of this invention is to provide a method for fluoriding catalysts with a fluoriding system employing as fluoriding agent materials heretofore considered inert.

Still another object of this invention is to provide a hydrocarbon conversion process undertaken in the presence of a catalyst prepared or regenerated in situ under non-corrosive conditions in a hydrocarbon conversion reactor.

Other objects and advantages will become apparent from a reading of the following detailed description and examples.

SUMMARY OF THE INVENTION Broadly, this invention contemplates a method of preparing a catalyst comprising a hydrogenating component, alumina and from about 0.5 to 15.0 weight percent fluorine which comprises contacting alumina having associated therewith a hydrogenating component selected from the group consisting of metals of Groups VIB, VIIB and VIII of the Periodic Table, their compounds and mixtures thereof with a combination of hydrogen and sulfuryl fluoride or thionyl fluoride at a temperature of from about 200 to I200F.

According to our invention, catalytically active fluoride catalysts can be prepared employing sulfuryl fluoride or thionyl fluoride, compounds heretofore considered chemically inert. It has been found that these compounds are rendered chemically reactive in the presence of a hydrogenating component comprising the metals and compounds of Groups VIB, VIIB and VIII and hydrogen such that an alumina composite can be activated and provided with a chemically combined fluorine content of from about 0.5 to 15.0, preferably 0.5 to 6.0 weight percent based on the catalyst.

The highly active hydrocarbon conversion catalysts contemplated herein are prepared from an alumina composite activated with a combination of hydrogen and one of the aforementioned fluorides. As indicated above, the alumina has associated therewith as a com ponent of the composite a member selected from the groupof metals of Groups VIB, VIIB and VIII of the Periodic Table exemplified by chromium, molybdenum, tungsten, rhenium, cobalt, nickel, platinum, palladium, ruthenium and rhodium. Combinations of metals are also contemplated such as platinum-rhenium, nickel-tungsten and cobalt-molybdenum. Themember may be present on the catalyst as metal or as a compound such as the oxide, sulfide or salt such as the sulfate. Preferably we employ a member having hydrogenating activity such as the metals of Group VIII and we particularly prefer platinum and palladium. In general, the catalyst may contain a member of Groups VIB, VIIB or VIII in amounts of from 0.01 to 30 weight percent calculated as weight of metal. When Group VIII members such as platinum, palladium, rhodium and ruthenium are employed as composite components we preferably employ from 0.1 to 2.0 weight percent. Combinations of metals such as nickel and tungsten are employed in greater amounts as for example 20 to 30 weight percent.

Aluminas in various forms may be used in this invention and particularly those aluminas having replaceable ing surface areas of from 50 to 400 square meters per gram and particularly etaand gamma-alumina. Suitable composites contemplated for contacting with our fluoriding system include commercially available materials including platinum-alumina and platinumrhenium-alumina reforming catalysts, chrome-alumina dehydrogenation catalysts and nickel-tungstenalumina, nickeI-tungsten-silica-aluminahydrogenation catalysts. The composites are prepared by techniques well known to the art. Illustratively, a metal, such as platinum, is provided to the composite by impregnating active alumina with an aqueous solution of chloropla-' tinic acid and ethylene diamine followed by drying and calcining at about l,050F. for 2 hours thereby providing a platinized alumina composite. Where palladium is contemplated, it may similarly be introduced by providing a palladium tetramine complex as by dissolving ods of at least 2 hours. Nickel oxide on alumina can be prepared by adding an aqueous solution of nickel nitrate to alumina at temperatures of from 80 to 200F. and calcining the dried composite at 800F. In a similar manner, Group VlB and VllB members are provided to the composite by impregnation with soluble salts of these metals, followed by calcination at 600 to l,200F. for several hours.

In accordance with our invention, a composite as hereinabove defined is contacted with a combination of hydrogen and sulfuryl fluoride or thionyl fluoride to introduce to the final catalyst about 0.5 to 15.0 weight percent chemically combined fluoride. Fluoriding in accordance with this invention enhances the acidity of the treated composite thereby promoting the catalysts activity and improving its selectivity. Moreover, fluoriding provides the catalyst with activity at lower temperatures where the unfluorided composite would be inactive.

The mole ratio of hydrogen to fluoride compound during the contacting stage can vary from 0.] to 100 moles of hydrogen per mole of fluoride compound and preferably within the range of 2 to moles of hydrogen per mole of fluoride compound. Mole ratios of hydrogen less than 0111 are undesirable because there is inefficient utilization ofthe fluoride compound and ratios above l00:l are, unnecessary because this greatly exceeds the optimum requirements of hydrogen consumption. The activating combination of hydrogen and fluoride compound may be introduced to the composite separately or as mixed gaseous streams and the gaseous activator components are permitted to flow through and over the composite. During contacting, the composite is generally maintained at a temperature of from 200 to l,200F. and preferably at a temperature of from about 600 to 900F. Depending on the activating temperature employed and the weight percent fluorine to be introduced to the composite, contact times ranging from /2 to 24 hours are employed. In view of the non-corrosive nature of these fluoride compounds, the catalyst can be prepared in situ in a hydrocarbon conversion reactor by passing a stream of hydrogen and the fluoride compound to the vessel directly containing the composite. The effluent from the reactor during activation contains hydrogen sulfide, water and 'unreacted components.

As mentioned above, the composite is contacted with a combination of hydrogen and sulfuryl fluoride or thionyl fluoride. in the absence of the aforementioned Group VlB. VllB and Vlll members as a component of the composite the fluoride compound is chemically inactive, particularly at temperatures of 900F. and below, and the alumina is merely provided with absorbed fluoride compound and not chemically combined fluorine. Merely absorbing the compound onto the compositedoes not provide or promote activity nor improve selectivity. Unexpectedly, composites of alumina associated with a Group VlB, VllB or Vlll metal as described above when contacted with a combination of hydrogen and the fluoride compound in some manner unknown to applicants permits reaction between the heretofore considered inert fluoride compound and the composite such that chemically combined fluorine is introduced to the composite thereby providing the contemplated catalytically active material. Contacting as set out above is broadly undertaken at a temperature 7 of at least 200 and up to 1,200F. Preferably, initial contacting of the composite, hydrogen and fluoride compound is conducted as temperatures of at least 450F. thereby initiating rapid fluoriding of the composite. Upon reaching a fluoride content of about 0.5 weight percent, subsequent contacting temperatures as low as 200F. can be employed. However, at the lower temperatures the reaction is slow and results in inefficient use of fluoride compound. lnitial or subsequent contact temperatures below 200F. are generally insufficient to provide adequate reaction rates or highly active catalysts useful for commercial size operations in that fluoride levels of less than 0.5 weight percent result. In our highly preferred embodiment allcontacting is conducted at temperatures of from about 600 to 900F.

As contemplated herein, the inventive concept includes both initial activation and subsequent regeneration of the fluorided catalysts. It will be appreciated that during the course of hydrocarbon conversion, feedstocks employed may in some instances contain materials such as combined nitrogen in amounts exceeding 30 ppm or such other materials as sulfur 0r carbonaceous deposits which in the course of operation cause the catalyst to become deactivated. These deactivating materials are removed from the catalyst by a hydrogen strip or a controlled oxidation. The catalyst surface is then exposed to a regenerating procedure by contacting with the combination of hydrogen and fluoride compound in the manner described above.

The catalyst prepared by our invention can be produced in pellet, granular, bead or pulverulent form to facilitate its use in fixed beds, moving beds or fluidized solid beds as is well known in the art. During the course of catalyst activation or regeneration, the effluent from the hydrocarbon conversion reactor consists largely of hydrogen sulfide, water, hydrogen and unconverted fluoride compound. Any unconverted fluoride compound and excess hydrogen may be recycled.

The catalyst prepared herein is highly active for hydrocarbon conversion at relatively low temperatures of from 200 to l,000F. and finds application in a broad spectrum of conversion processes including hydrocracking, selective hydrocracking, hydroisomerization,

disproportionation, alkylation, polymerization, reforma ing and hydrogenation. In general, the hydrocarbon feedstocks contain less than 30 ppm nitrogen and are converted in the presence of our catalyst at temperatures recited above.

Catalysts prepared according to our invention are admirably suited to convert a wide range of hydrocarbon materials. lllustratively, fluorided platinized aluminas are highly active for hydrocracking and hydroisomerizing such charge materials as waxes, slack wax and middle distillate oils at temperatures of 550 to 800F., at

pressures of 300 to 750 pounds per square inch gauge,

liquid hourly space velocities of l to 20 and in the presence of hydrogen. ln'general, catalysts containing lower fluorine contents require the higher conversion temperatures for equivalent rates of reaction. Selectivity for isomerization of normal C to C paraffins is improved at the lower temperatures. Aromatics can be hydrogenated and lubricating oil fractions can be modified to improve viscosity indexand pour point. Fluorided aluminas having metal compounds such as the oxides associated therewith, exemplified by chromia and molybdena fluorided aluminas, show substantial activity for disproportionation of aromatics as for example the conversion of toluene to benzene and xylene at 750 to 1,000F. The catalysts are active for alkylation of aromatics and aliphatics and polymerization of olefins at temperatures of 200 to 400F. and pressures of 300 to 800 p.s.i.g. The fluorided catalysts are active for hydrocarbon conversions at considerably lower temperatures than the non-fluorided composite. For example, fluorided platinized alumina permits isomerization of C to C n-paraffins at the 600F. range whereas the non-fluorided composite is inactive at temperatures below 800F.

1n order to more fully illustrate the nature of our invention and manner of practicing the same, the followingexamples are presented. In these examples, the best mode contemplated by us for carrying out our invention is set forth:

EXAMPLE I 121 grams of commercially available 0.47 weight percent platinum on eta-alumina were treated at 800F. with 14 grams of sulfuryl fluoride added as a gaseous stream at the rate of one liter per hour for a period of 3 hours. Analysis of the effluent stream failed to detect hydrogen sulfide. On analysis of the composite, it was found to contain 1.74 weight percent absorbed fluorine and 1.82 weight percent sulfur. No chemically combined fluorine was detected.

EXAMPLE 11 143 grams of gamma-alumina were contacted with a stream of sulfuryl fluoride and hydrogen introduced at the rates respectively of 1.5 liters per hour and 30 liters per hour at a temperature of from 600 to 950F. Analysis of the effluent stream failed to detect hydrogen sulfide. Analysis ofthe gamma-alumina found it to contain 3.4 weight percent absorbed fluorine and 2 weight percent sulfur. No chemically combined fluorine was detected.

EXAMPLE I11 120 grams of 0.49 weight percent platinum on etaalumina were placed in a horizontal furnace tube and calcined at 800F. for a period of two hours. Sulfuryl fluoride and hydrogen were introduced at the rates respectively of 1 liter and 5 liters per hour for a period of 3 hours at a temperature of 800F. Analysis of the gaseous effluent showed it to contain hydrogen sulfide. On analysis of the catalyst, it was found to contain 0.8 weight percent chemically combined fluorine and 0.25 weight percent sulfur.

EXAMPLE IV 126 grams of 0.3 weight percent palladium on etaalumina were heated at 800F. under a hydrogen atmosphere flowing at the rate of 30 liters per hour for 15 minutes. Hydrogen and sulfuryl fluoride were introduced at the rates respectively of 1 to 2 liters per hour and 30 liters per hour for a period of 2 hours at a temperature of 800F. Analysis of the gaseous effluent lar operator, the availability of the metal, etc. The actishowedit to contain hydrogen sulfidepon analysis of the catalyst it was found to contain 1.73 weight percent chemically combined fluorine and 0.1 weight percent sulfur.

EXAMPLE V In a manner similar to Example IV, 0.49 weight percent platinum on eta-alumina was contacted with hydrogen and sulfuryl fluoride introduced at the rates respectively of l to 2 liters per hour and 30 liters per hour for a period of 2 hours at a temperature of 800F. On analysis the catalyst was found to contain 2.8 weight percent chemically combined fluorine.

EXAMPLE VI TABLE I Catalyst Example Temperature F. Percent Conversion lll 550 18.0 W 550 14.7 V 550 26.3

From the data above, the catalysts have significant activity under low temperature conversion conditions.

As fluorine content of the catalyst is increased, that is up to 15.0 weight percent, significant increases in catalytic activity are provided.

From the foregoing, it can be seen that we have provided a significantly useful process for the preparation of a hydrocarbon conversion catalyst. Our catalyst is particularly useful in the isomerization if isomerizable hydrocarbons especially paraffinic hydrocarbons in the C to C range. Our catalyst can also be used in alkylation processes without varying the manipulative procedures to accommodate the catalyst prepared by our invention. It is seen that our process can be performed in situ, i.e., within the hydrocarbon conversion reactor itself and does not necessitate withdrawal of catalyst from the vessel for transfer to the hydrocarbon ,conversion reactor with the attendant problem of subjecting the catalyst to moisture. It should be further noted that our process can be performed to regenerate a spent catalyst by first heating the spent catalyst to decarbonize the catalyst and then treating in the manner of our invention. Our process can be performedwithout the use of expensive chemicals, high pressures or temperatures and is thus suited for commercial operation, The catalyst can contain any one of the aforementioned metals, for example, platinum, palladium, ruthenium and rhodium depending upon the choice of the particuvation of the catalyst base containing any of these metals proceeds essentially in the same way of activation of alumina base catalyst containing another metal of the group. Thus the manipulative procedure does not substantially vary from one metal to the other. 1

The terms and expressions which have been used herein are terms of description and not of limitation as there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof as it is recognized that various modifications are possible within the scope of the invention.

We claim:

1. An isomerization process which comprises contacting a feedstock containing C m to C H hydrocarbons at a temperatureof from 200 to 1,000F in the presence of hydrogen with a catalyst comprising a hydrogenating component, alumina and from about 0.5 to 15.0 weight percent fluorine, said catalyst prepared or regenerated by contacting alumina having associated therewith a hydrogenating component selected from the group consisting of the metals, oxides, sulfides and salts of the metals of Groups VlB, VllB and VIII of the Periodic Table and mixtures thereof with a combination of hydrogen and a fluoride compound selected from the group consisting of sulfuryl fluoride and thionyl fluoride at a temperature of from about 200 to l,200F.

2. A process according to claim 1 wherein said fluoride compound is sulfuryl fluoride.

3. A process according to claim 1 wherein said fluoride compound is thionyl fluoride.

4. A process according to claim 1 wherein said hy drogenating component is present in said catalyst in an amount of from 0.01 to 30.0 weight percent calculated as weight of metal. I

5. A process according to claim 1 wherein said component is selected from the group consisting of platinum, palladium, rhodium and ruthenium and where said component is present in said catalyst in an amount of from 0.1 to 2.0 weight percent.

6. A process according to claim 1 wherein said component comprises platinum and rhenium.

7. A process according to claim 1 wherein the mole ratio of said hydrogen to said fluoride compound is from 0.1:1 to :1.

8. A process according to claim 1 wherein said temperature is from 600 to 900F.

9. A process according to claim 1 wherein said alumina is eta-alumina.

10. A process according to claim 1 wherein said alumina is gamma-alumina. 

1. AN ISOMERIZATION PROCESS WHICH COMPRISES CONTACTING A FEEDSTOCK CONTAINING C10 TO C14 HYDROCARBONS AT A TEMPERATURE OF FROM 200* TO 1,000*F. IN THE PRESENCE OF HYDROGEN WITH A CATALYST COMPRISING A HYDROGENATING COMPONENT, ALUMINA AND FROM ABOUT 0.5 TO 15.0 WEIGHT PERCENT FLUORINE, SAID CATALYST PREPARED OR REGENERATED BY CONTACTING ALUMINA HAVIG ASSOCIATED THEREWITH A HYDROGENATING COMPONENT SELECTED FROM THE GROUP CONSISTING OF THE METALS, OXIDES, SULFIDES AND SALTS OF THE METALS OF GROUP VIB, VIIB AND VIII OF THE PERIODIC TABLE AND MIXTURES THEREOF WITH A COMBINATION OF HYDROGEN AND A FLUORIDE COMPOUND SELECTED FROM THE GROUP CONSISTING OF SULFURYL FLUORIDE AND THIONYL FLUORIDE AT A TEMPERATURE OF FROM ABOUT 200* TO 1,200*F.
 2. A process according to claim 1 wherein said fluoride compound is sulfuryl fluoride.
 3. A process according to claim 1 wherein said fluoride compound is thionyl fluoride.
 4. A process according to claim 1 wherein said hydrogenating component is present in said catalyst in an amount of from 0.01 to 30.0 weight percent calculated as weight of metal.
 5. A process according to claim 1 wherein said component is selected from the group consisting of platinum, palladium, rhodium and ruthenium and where said component is present in said catalyst in an amount of from 0.1 to 2.0 weight percent.
 6. A process according to claim 1 wherein said component comprises platinum and rhenium.
 7. A process according to claim 1 wherein the mole ratio of said hydrogen to said fluoride compound is from 0.1:1 to 100:1.
 8. A process according to claim 1 wherein said temperature is from 600* to 900*F.
 9. A process according to claim 1 wherein said alumina is eta-alumina.
 10. A process according to claim 1 wherein said alumina is gamma-alumina. 